Hronologija gubitka integriteta konstrukcija zbog grešaka izrade zavarenih konstrukcija / Chronology of lost structural integrity initiated from manufacturing defects in welded structures
(Institut za ispitivanje materijala, Beograd, 2009)
U različitim vremenskim periodima dolazilo je do gubitka integriteta zavarenih konstrukcija zbog razvoja proizvodnih grešaka zavarenog spoja. Mehanizmi otkaza su bili različiti i uvek su predstavljali novo iskustvo, koje ...
Quantification of stress raiser influence on decrease of machine parts fatigue life
(Univ Novi Sad, Fac Tech Sci, Adeko, Novi Sad, 2012)
This paper displays the usage of Theory of Critical Distances (TCD) in the prediction of high-cycle fatigue behaviour in machine parts and systems. It is possible to gain real overview of stresses of machine parts by Finite ...
Prediction of crack initiation in spur gear contact zone
(Univ Novi Sad, Fac Tech Sci, Adeko, Novi Sad, 2012)
The objective of this paper is to give a new viewpoint in contact fatigue prediction in the case of high-cycle fatigue. The presented research is based on up-to-date methods and multidisciplinary approach, and enables ...
Uticaj prsline na karakteristike zavarenog spoja pri različitim vrstama opterećenja / Influence of crack on welded joint characteristics in different types of loads
(Vojnotehnički institut, Beograd, 2018)
Primena čelika visoke čvrstoće kod projektovanja zavarenih konstrukcija zahteva podatke o svojstvima istih pri različitim uslovima opterećenja. Zahvaljujući visokom naponu tečenja debljina zida može se smanjiti u poređenju ...
A new methodology for prediction of high-cycle contact fatigue for spur gears
(Univerzitet u Novom Sadu - Fakultet tehničkih nauka, Novi Sad, 2012)
High-cycle contact fatigue is a localized phenomenon that occurs in highly stressed grains of the material on or under the contact region. The contact zones of tooth flanks for meshed gears are subjected to contact fatigue ...
Methodology of determination the influence of corrosion pit on decrease of hydro turbine shaft fatigue life
(Univerzitet u Novom Sadu - Fakultet tehničkih nauka, Novi Sad, 2012)
This paper describes the influence of corrosion on stress concentration factor and crack initiation at shaft flange transition section. The case study of hydraulic turbine shaft failure is used as the basis for this research. ...
Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels
(Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK), 2018)
The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.
Basic requirements for cleaner steels and lower energy consumption during production induce that ...
Analysis of contact fatigue coupled with geometry and material nonlinearities by Theory of critical distances
(2nd Conference on Nonlinearity, Belgrade, 2022)
The contact fatigue is a localized phenomenon that occurs in highly
stressed local zone of the material under the loaded contact region and as such is
highly nonlinear problem. This phenomenon exists in almost all real ...
Presence of crack due the constant exploitation of turbine shaft
(Advanced Technologies & Materials, 2023)
Designing, constructing and putting into operation a hydroelectric power plant includes complex
tasks. Stresses of turbine and hydromechanical equipment of hydro power plants arise during the
production of parts and ...
Occurrence of cracks due to inadequate turbine shaft construction
(Proceedings of the 16th International Conference on Accomplishments in Mechanical and Industrial Engineering -DEMI 2023, 2023)
After several decades of constant exploitation of the horizontal bulb turbine, which is an integral
part of the hydroelectric power unit, empirically, the formation of a crack occurs in the turbine shaft
due to the ...