TY  - JOUR
AU  - Sedmak, Simon
AU  - Arsić, Miodrag
AU  - Bajić, Darko R.
AU  - Mladenović, Mladen
AU  - Savić, Zoran
PY  - 2015
UR  - http://rims.institutims.rs/handle/123456789/262
AB  - Presented are results of non-destructive tests performed on the parent material and welded joints of structural parts of a breeches pipe (collar and anchor), and results of destructive tests performed on the parent material of the anchor. Non-destructive testing included visual (VT), mag-netic particle (MT), and ultrasonic testing (UT), while destructive tests included determination of chemical com-position, tensile properties, impact energy and hardness. Based on test results it is established that the major cause for the occurrence of damage in the carrying structure of the breeches pipe no.1 of pipeline III, or in other words, the degradation of anchor parent material and welded joints between the collar and anchor, and between the pipeline and anchor, is in the fact that the breeches pipe started to lean, not on the collar, as specified by design, but on the anchor that could not endure all loads occurring in service.
PB  - Institut za ispitivanje materijala, Beograd
T2  - Structural Integrity and Life
T1  - Analysis of causes of degradation of parent material and weld metal of breeches pipe at hydro power plant 'Perućica'
EP  - 151
IS  - 3
SP  - 147
VL  - 15
UR  - https://hdl.handle.net/21.15107/rcub_rims_262
ER  - 

@article{
author = "Sedmak, Simon and Arsić, Miodrag and Bajić, Darko R. and Mladenović, Mladen and Savić, Zoran",
year = "2015",
abstract = "Presented are results of non-destructive tests performed on the parent material and welded joints of structural parts of a breeches pipe (collar and anchor), and results of destructive tests performed on the parent material of the anchor. Non-destructive testing included visual (VT), mag-netic particle (MT), and ultrasonic testing (UT), while destructive tests included determination of chemical com-position, tensile properties, impact energy and hardness. Based on test results it is established that the major cause for the occurrence of damage in the carrying structure of the breeches pipe no.1 of pipeline III, or in other words, the degradation of anchor parent material and welded joints between the collar and anchor, and between the pipeline and anchor, is in the fact that the breeches pipe started to lean, not on the collar, as specified by design, but on the anchor that could not endure all loads occurring in service.",
publisher = "Institut za ispitivanje materijala, Beograd",
journal = "Structural Integrity and Life",
title = "Analysis of causes of degradation of parent material and weld metal of breeches pipe at hydro power plant 'Perućica'",
pages = "151-147",
number = "3",
volume = "15",
url = "https://hdl.handle.net/21.15107/rcub_rims_262"
}

Sedmak, S., Arsić, M., Bajić, D. R., Mladenović, M.,& Savić, Z.. (2015). Analysis of causes of degradation of parent material and weld metal of breeches pipe at hydro power plant 'Perućica'. in Structural Integrity and Life
Institut za ispitivanje materijala, Beograd., 15(3), 147-151.
https://hdl.handle.net/21.15107/rcub_rims_262

Sedmak S, Arsić M, Bajić DR, Mladenović M, Savić Z. Analysis of causes of degradation of parent material and weld metal of breeches pipe at hydro power plant 'Perućica'. in Structural Integrity and Life. 2015;15(3):147-151.
https://hdl.handle.net/21.15107/rcub_rims_262 .

Sedmak, Simon, Arsić, Miodrag, Bajić, Darko R., Mladenović, Mladen, Savić, Zoran, "Analysis of causes of degradation of parent material and weld metal of breeches pipe at hydro power plant 'Perućica'" in Structural Integrity and Life, 15, no. 3 (2015):147-151,
https://hdl.handle.net/21.15107/rcub_rims_262 .

TY  - JOUR
AU  - Veljić, Darko M.
AU  - Sedmak, Aleksandar
AU  - Rakin, Marko
AU  - Bajić, Nikola S.
AU  - Međo, Bojan
AU  - Bajić, Darko R.
AU  - Grabulov, Vencislav
PY  - 2014
UR  - http://rims.institutims.rs/handle/123456789/237
AB  - This paper presents experimental and numerical analysis of the change of temperature and force in the vertical direction during the friction stir welding of high-strength aluminium alloy 2024 T3. This procedure confirmed the correctness of the numerical model, which is subsequently used for analysis of the temperature field in the welding zone, where it is different to determine the temperature experimentally. 3D finite element model is developed using the software package Abaqus; arbitrary Lagrangian-Eulerian formulation is applied. Johnson-Cook material law and Coulomb's Law of friction are used for modelling the material behaviour. Temperature fields are symmetrical with respect to the welding line. The temperature values below the tool shoulder, i.e. in the welding zone, which are reached during the plunge stage, are approximately constant during the entire welding process and lie within the interval 430-502 degrees C. The temperature of the material in the vicinity of the tool is about 500 degrees C, while the values on the top surface of the welding plates (outside the welding zone, but close to the tool shoulder) are about 400 degrees C. The temperature difference between the top and bottom surface of the plates is small, 10-15 degrees C.
PB  - Univerzitet u Beogradu - Institut za nuklearne nauke Vinča, Beograd
T2  - Thermal Science
T1  - Experimental and numerical thermo - mechanical analysis of friction stir welding of high - strength alluminium alloy
EP  - S38
SP  - S29
VL  - 18
DO  - 10.2298/TSCI130512171V
ER  - 

@article{
author = "Veljić, Darko M. and Sedmak, Aleksandar and Rakin, Marko and Bajić, Nikola S. and Međo, Bojan and Bajić, Darko R. and Grabulov, Vencislav",
year = "2014",
abstract = "This paper presents experimental and numerical analysis of the change of temperature and force in the vertical direction during the friction stir welding of high-strength aluminium alloy 2024 T3. This procedure confirmed the correctness of the numerical model, which is subsequently used for analysis of the temperature field in the welding zone, where it is different to determine the temperature experimentally. 3D finite element model is developed using the software package Abaqus; arbitrary Lagrangian-Eulerian formulation is applied. Johnson-Cook material law and Coulomb's Law of friction are used for modelling the material behaviour. Temperature fields are symmetrical with respect to the welding line. The temperature values below the tool shoulder, i.e. in the welding zone, which are reached during the plunge stage, are approximately constant during the entire welding process and lie within the interval 430-502 degrees C. The temperature of the material in the vicinity of the tool is about 500 degrees C, while the values on the top surface of the welding plates (outside the welding zone, but close to the tool shoulder) are about 400 degrees C. The temperature difference between the top and bottom surface of the plates is small, 10-15 degrees C.",
publisher = "Univerzitet u Beogradu - Institut za nuklearne nauke Vinča, Beograd",
journal = "Thermal Science",
title = "Experimental and numerical thermo - mechanical analysis of friction stir welding of high - strength alluminium alloy",
pages = "S38-S29",
volume = "18",
doi = "10.2298/TSCI130512171V"
}

Veljić, D. M., Sedmak, A., Rakin, M., Bajić, N. S., Međo, B., Bajić, D. R.,& Grabulov, V.. (2014). Experimental and numerical thermo - mechanical analysis of friction stir welding of high - strength alluminium alloy. in Thermal Science
Univerzitet u Beogradu - Institut za nuklearne nauke Vinča, Beograd., 18, S29-S38.
https://doi.org/10.2298/TSCI130512171V

Veljić DM, Sedmak A, Rakin M, Bajić NS, Međo B, Bajić DR, Grabulov V. Experimental and numerical thermo - mechanical analysis of friction stir welding of high - strength alluminium alloy. in Thermal Science. 2014;18:S29-S38.
doi:10.2298/TSCI130512171V .

Veljić, Darko M., Sedmak, Aleksandar, Rakin, Marko, Bajić, Nikola S., Međo, Bojan, Bajić, Darko R., Grabulov, Vencislav, "Experimental and numerical thermo - mechanical analysis of friction stir welding of high - strength alluminium alloy" in Thermal Science, 18 (2014):S29-S38,
https://doi.org/10.2298/TSCI130512171V . .