AB  - Quantity of waste rubber generated by automobile tires is growing, posing an environmental threat. Rubber tire recycling was studied for usage in asphalt and waterproofing systems during past few decades. Globally, concrete is the most widely used building material. About 7% of CO2 emissions come from the cement production. The purpose of this research is to assess if using waste rubber and Portland cement together in composite material for structural applications is feasible. Waste tires (shredded to 0/1 mm) were used as fine aggregate replacement (in 2.5 and 7.5 %), together with PC and natural stone. An investigation of properties in fresh (slump test, bulk density, air content) and hardened state (bulk density, compressive strength) was performed on the rubberized concrete. The compressive strength decreased by increasing the rubber content for all w/c ratios (0.55-0.4). The addition of fine-sized rubber did not cause a retardation in cement hydration mechanism. According to the obtained compressive strengths, all designed rubberized concretes belong to a group of structural concretes.
PB  - Association for ETRAN Society
T2  - Science of Sintering Science of Sintering OnLine-First Issue
T1  - Investigation of the Mechanical Properties of Concrete Incorporating Recycled Rubber Particles
VL  - 0
DO  - 10.2298/SOS240523027S
ER  - 

@article{
author = "Stojanović, Marko and Šupić, Slobodan and Janković, Ksenija and Bojović, Dragan and Terzić, Anja and Malešev, Mirjana",
year = "2024",
abstract = "Quantity of waste rubber generated by automobile tires is growing, posing an environmental threat. Rubber tire recycling was studied for usage in asphalt and waterproofing systems during past few decades. Globally, concrete is the most widely used building material. About 7% of CO2 emissions come from the cement production. The purpose of this research is to assess if using waste rubber and Portland cement together in composite material for structural applications is feasible. Waste tires (shredded to 0/1 mm) were used as fine aggregate replacement (in 2.5 and 7.5 %), together with PC and natural stone. An investigation of properties in fresh (slump test, bulk density, air content) and hardened state (bulk density, compressive strength) was performed on the rubberized concrete. The compressive strength decreased by increasing the rubber content for all w/c ratios (0.55-0.4). The addition of fine-sized rubber did not cause a retardation in cement hydration mechanism. According to the obtained compressive strengths, all designed rubberized concretes belong to a group of structural concretes.",
publisher = "Association for ETRAN Society",
journal = "Science of Sintering Science of Sintering OnLine-First Issue",
title = "Investigation of the Mechanical Properties of Concrete Incorporating Recycled Rubber Particles",
volume = "0",
doi = "10.2298/SOS240523027S"
}

Stojanović, M., Šupić, S., Janković, K., Bojović, D., Terzić, A.,& Malešev, M.. (2024). Investigation of the Mechanical Properties of Concrete Incorporating Recycled Rubber Particles. in Science of Sintering Science of Sintering OnLine-First Issue
Association for ETRAN Society., 0.
https://doi.org/10.2298/SOS240523027S

Stojanović M, Šupić S, Janković K, Bojović D, Terzić A, Malešev M. Investigation of the Mechanical Properties of Concrete Incorporating Recycled Rubber Particles. in Science of Sintering Science of Sintering OnLine-First Issue. 2024;0.
doi:10.2298/SOS240523027S .

Stojanović, Marko, Šupić, Slobodan, Janković, Ksenija, Bojović, Dragan, Terzić, Anja, Malešev, Mirjana, "Investigation of the Mechanical Properties of Concrete Incorporating Recycled Rubber Particles" in Science of Sintering Science of Sintering OnLine-First Issue, 0 (2024),
https://doi.org/10.2298/SOS240523027S . .

TY  - CONF
AU  - Stojanović, Marko
AU  - Janković, Ksenija
AU  - Bojović, Dragan
AU  - Terzić, Anja
AU  - Šupić, Slobodan
PY  - 2024
UR  - http://rims.institutims.rs/handle/123456789/857
AB  - Waste tires have long been a challenge for waste disposal. In an effort to mitigate the impact of solid waste on the environment and recycle it as much as possible, research has been conducted into the possibility of using this waste in concrete mixes. However, the use of these waste materials in concrete is still not popular due to the lack of knowledge of the properties that can be obtained with this material. Hence, the aim is to use waste material in the production of concrete, and that concrete mixes with this material have satisfactory performance. The paper presents the results of research on concrete in which volume replacement of fine aggregate with crumb rubber was performed in the amount of 5%, and this concrete was compared with the control concrete mix and aerated concrete. All concrete are made with a water-cement factor of 0.45. The performance of fresh concrete was monitored for 10, 30 and 60 min. In the case of concrete with the addition of crumb rubber, after 60 min, higher values of air content were obtained, and lower values of volume mass of fresh concrete compared to the initial measurements. The obtained test results of hardened concrete indicate that concrete with crumb rubber has a lower compressive strength compared to the control concrete mix, while compared to aerated concrete, they obtain approximate compressive strength values.
PB  - University of Montenegro Faculty of Civil Engineering
C3  - The ninth international conference civil engineering science & practice, GNP 2024 proceedings, Kolašin, Montenegro
T1  - Properties of concrete with crumb rubber in relation to ordinary and aerated concrete
EP  - 617
SP  - 609
UR  - https://hdl.handle.net/21.15107/rcub_rims_857
ER  - 

@conference{
author = "Stojanović, Marko and Janković, Ksenija and Bojović, Dragan and Terzić, Anja and Šupić, Slobodan",
year = "2024",
abstract = "Waste tires have long been a challenge for waste disposal. In an effort to mitigate the impact of solid waste on the environment and recycle it as much as possible, research has been conducted into the possibility of using this waste in concrete mixes. However, the use of these waste materials in concrete is still not popular due to the lack of knowledge of the properties that can be obtained with this material. Hence, the aim is to use waste material in the production of concrete, and that concrete mixes with this material have satisfactory performance. The paper presents the results of research on concrete in which volume replacement of fine aggregate with crumb rubber was performed in the amount of 5%, and this concrete was compared with the control concrete mix and aerated concrete. All concrete are made with a water-cement factor of 0.45. The performance of fresh concrete was monitored for 10, 30 and 60 min. In the case of concrete with the addition of crumb rubber, after 60 min, higher values of air content were obtained, and lower values of volume mass of fresh concrete compared to the initial measurements. The obtained test results of hardened concrete indicate that concrete with crumb rubber has a lower compressive strength compared to the control concrete mix, while compared to aerated concrete, they obtain approximate compressive strength values.",
publisher = "University of Montenegro Faculty of Civil Engineering",
journal = "The ninth international conference civil engineering science & practice, GNP 2024 proceedings, Kolašin, Montenegro",
title = "Properties of concrete with crumb rubber in relation to ordinary and aerated concrete",
pages = "617-609",
url = "https://hdl.handle.net/21.15107/rcub_rims_857"
}

Stojanović, M., Janković, K., Bojović, D., Terzić, A.,& Šupić, S.. (2024). Properties of concrete with crumb rubber in relation to ordinary and aerated concrete. in The ninth international conference civil engineering science & practice, GNP 2024 proceedings, Kolašin, Montenegro
University of Montenegro Faculty of Civil Engineering., 609-617.
https://hdl.handle.net/21.15107/rcub_rims_857

Stojanović M, Janković K, Bojović D, Terzić A, Šupić S. Properties of concrete with crumb rubber in relation to ordinary and aerated concrete. in The ninth international conference civil engineering science & practice, GNP 2024 proceedings, Kolašin, Montenegro. 2024;:609-617.
https://hdl.handle.net/21.15107/rcub_rims_857 .

Stojanović, Marko, Janković, Ksenija, Bojović, Dragan, Terzić, Anja, Šupić, Slobodan, "Properties of concrete with crumb rubber in relation to ordinary and aerated concrete" in The ninth international conference civil engineering science & practice, GNP 2024 proceedings, Kolašin, Montenegro (2024):609-617,
https://hdl.handle.net/21.15107/rcub_rims_857 .