TY  - CONF
AU  - Ćosić, Milena
AU  - Aćimović-Pavlović, Zagorka
AU  - Terzić, Anja
AU  - Dojčinović, Marina
AU  - Pavlović, Ljubica
PY  - 2012
UR  - http://rims.institutims.rs/handle/123456789/166
AB  - The aim of this study was to investigate the influence of various process parameters on the microstructure of composite materials based on alloys All 8Wt%Si with the addition of 10Wt%SiC. The effect of stirring speed (1000 and 1500 rpm), stirring time 15 min and casting temperature 565 degrees C on the structural and mechanical properties are discussed. It was found that applying the stirring speed of 1500 rpm in semisolid state the best distribution of SiC particles in the matrix was achieved, which gave satisfying mechanical properties. In order to evaluate the quality of obtained composites and their possible application in the practice, tests were carried out under conditions of cavitation. Cavitation damage to the composite samples was determined using modified vibratory cavitation equipment. Mass loss and surface analysis of composite samples during the experiment were used as an indicator the level of cavitation damage. The results showed very good cavitation resistance which gives the possibility of using these materials in condition where cavitation resistance is needed.
PB  - ModTech Publishing House
C3  - Modtech 2012: New Face of T M C R, Vols I and II
T1  - The possibility of obtaining. Composite al18wt%si/sic by compocasting process
EP  - 252
SP  - 249
UR  - https://hdl.handle.net/21.15107/rcub_technorep_2164
ER  - 

@conference{
author = "Ćosić, Milena and Aćimović-Pavlović, Zagorka and Terzić, Anja and Dojčinović, Marina and Pavlović, Ljubica",
year = "2012",
abstract = "The aim of this study was to investigate the influence of various process parameters on the microstructure of composite materials based on alloys All 8Wt%Si with the addition of 10Wt%SiC. The effect of stirring speed (1000 and 1500 rpm), stirring time 15 min and casting temperature 565 degrees C on the structural and mechanical properties are discussed. It was found that applying the stirring speed of 1500 rpm in semisolid state the best distribution of SiC particles in the matrix was achieved, which gave satisfying mechanical properties. In order to evaluate the quality of obtained composites and their possible application in the practice, tests were carried out under conditions of cavitation. Cavitation damage to the composite samples was determined using modified vibratory cavitation equipment. Mass loss and surface analysis of composite samples during the experiment were used as an indicator the level of cavitation damage. The results showed very good cavitation resistance which gives the possibility of using these materials in condition where cavitation resistance is needed.",
publisher = "ModTech Publishing House",
journal = "Modtech 2012: New Face of T M C R, Vols I and II",
title = "The possibility of obtaining. Composite al18wt%si/sic by compocasting process",
pages = "252-249",
url = "https://hdl.handle.net/21.15107/rcub_technorep_2164"
}

Ćosić, M., Aćimović-Pavlović, Z., Terzić, A., Dojčinović, M.,& Pavlović, L.. (2012). The possibility of obtaining. Composite al18wt%si/sic by compocasting process. in Modtech 2012: New Face of T M C R, Vols I and II
ModTech Publishing House., 249-252.
https://hdl.handle.net/21.15107/rcub_technorep_2164

Ćosić M, Aćimović-Pavlović Z, Terzić A, Dojčinović M, Pavlović L. The possibility of obtaining. Composite al18wt%si/sic by compocasting process. in Modtech 2012: New Face of T M C R, Vols I and II. 2012;:249-252.
https://hdl.handle.net/21.15107/rcub_technorep_2164 .

Ćosić, Milena, Aćimović-Pavlović, Zagorka, Terzić, Anja, Dojčinović, Marina, Pavlović, Ljubica, "The possibility of obtaining. Composite al18wt%si/sic by compocasting process" in Modtech 2012: New Face of T M C R, Vols I and II (2012):249-252,
https://hdl.handle.net/21.15107/rcub_technorep_2164 .

TY  - JOUR
AU  - Ćosić, Milena
AU  - Aćimović-Pavlović, Zagorka
AU  - Terzić, Anja
AU  - Nedeljković, Borivoje
AU  - Pavlović, Ljubica
PY  - 2012
UR  - http://rims.institutims.rs/handle/123456789/179
AB  - Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests showed that two major changes of microstructural properties of rheocasting alloy, in comparison with conventional alloy, are change of dendrite morphology into nondendrite one and change of primary phases size (alpha-Al and Si). Both changes of primary particles were monitored in area near the stirrer and at a small distance from the crucible wall. Test showed that sizes of primary, alpha-Al particles decreased with stirring speed increment, while roundness of particles increased with stirring speed increment. Stirring speed change led to different degree of primary Si particles agglomeration. At stirring speed 1000 rpm, Si particles are uniformly distributed, while at speed 1500 rpm, a tendency to form clusters is more expressed. Test results were discussed on basis of utilizing fragmentation-agglomeration mechanism of primary phase evolution in a semi-solid melt, which may contribute to explanation of semi-solid structure development.
PB  - Editura Stiintifica Fmr, Bucharest
T2  - Metalurgia International
T1  - Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process
EP  - 93
IS  - 3
SP  - 88
VL  - 17
UR  - https://hdl.handle.net/21.15107/rcub_rims_179
ER  - 

@article{
author = "Ćosić, Milena and Aćimović-Pavlović, Zagorka and Terzić, Anja and Nedeljković, Borivoje and Pavlović, Ljubica",
year = "2012",
abstract = "Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests showed that two major changes of microstructural properties of rheocasting alloy, in comparison with conventional alloy, are change of dendrite morphology into nondendrite one and change of primary phases size (alpha-Al and Si). Both changes of primary particles were monitored in area near the stirrer and at a small distance from the crucible wall. Test showed that sizes of primary, alpha-Al particles decreased with stirring speed increment, while roundness of particles increased with stirring speed increment. Stirring speed change led to different degree of primary Si particles agglomeration. At stirring speed 1000 rpm, Si particles are uniformly distributed, while at speed 1500 rpm, a tendency to form clusters is more expressed. Test results were discussed on basis of utilizing fragmentation-agglomeration mechanism of primary phase evolution in a semi-solid melt, which may contribute to explanation of semi-solid structure development.",
publisher = "Editura Stiintifica Fmr, Bucharest",
journal = "Metalurgia International",
title = "Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process",
pages = "93-88",
number = "3",
volume = "17",
url = "https://hdl.handle.net/21.15107/rcub_rims_179"
}

Ćosić, M., Aćimović-Pavlović, Z., Terzić, A., Nedeljković, B.,& Pavlović, L.. (2012). Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process. in Metalurgia International
Editura Stiintifica Fmr, Bucharest., 17(3), 88-93.
https://hdl.handle.net/21.15107/rcub_rims_179

Ćosić M, Aćimović-Pavlović Z, Terzić A, Nedeljković B, Pavlović L. Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process. in Metalurgia International. 2012;17(3):88-93.
https://hdl.handle.net/21.15107/rcub_rims_179 .

Ćosić, Milena, Aćimović-Pavlović, Zagorka, Terzić, Anja, Nedeljković, Borivoje, Pavlović, Ljubica, "Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process" in Metalurgia International, 17, no. 3 (2012):88-93,
https://hdl.handle.net/21.15107/rcub_rims_179 .