RIMS - Repository of Institute for Material Testing
Institute for Material Testing
    • English
    • Српски
    • Српски (Serbia)
  • English 
    • English
    • Serbian (Cyrillic)
    • Serbian (Latin)
  • Login
View Item 
  •   RIMS
  • Institut za ispitivanje materijala
  • Radovi istraživača / Researchers' publications
  • View Item
  •   RIMS
  • Institut za ispitivanje materijala
  • Radovi istraživača / Researchers' publications
  • View Item
JavaScript is disabled for your browser. Some features of this site may not work without it.

Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process

No Thumbnail
Authors
Ćosić, Milena
Aćimović-Pavlović, Zagorka
Terzić, Anja
Nedeljković, Borivoje
Pavlović, Ljubica
Article (Published version)
Metadata
Show full item record
Abstract
Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests showed that two major changes of microstructural properties of rheocasting alloy, in comparison with conventional alloy, are change of dendrite morphology into nondendrite one and change of primary phases size (alpha-Al and Si). Both changes of primary particles were monitored in area near the stirrer and at a small distance from the crucible wall. Test showed that sizes of primary, alpha-Al particles decreased with stirring speed increment, while roundness of particles increased with stirring speed increment. Stirring speed change led to different degree of primary Si particles agglomeration. At stirring speed 1000 rpm, Si particles are uniformly distributed, while at speed 1500 rpm, a tendency to form clusters is more expressed. Test results were discussed on basis of... utilizing fragmentation-agglomeration mechanism of primary phase evolution in a semi-solid melt, which may contribute to explanation of semi-solid structure development.

Keywords:
rheocasting / primary silicon / microstructure / mechanical stirring / aluminium silicon alloy
Source:
Metalurgia International, 2012, 17, 3, 88-93
Publisher:
  • Editura Stiintifica Fmr, Bucharest
Funding / projects:
  • The development of casting technologies under the influence of electromagnetic field and technologies of hot plastic forming of 7000 series aluminium alloys for special purposes (RS-34002)
  • Directed synthesis, structure and properties of multifunctional materials (RS-172057)
  • Development and application of multifunctional materials using domestic raw materials in upgraded processing lines (RS-45008)

ISSN: 1582-2214

WoS: 000300597300017

Scopus: 2-s2.0-84857014394
[ Google Scholar ]
1
Handle
https://hdl.handle.net/21.15107/rcub_rims_179
URI
http://rims.institutims.rs/handle/123456789/179
Collections
  • Radovi istraživača / Researchers' publications
Institution/Community
Institut za ispitivanje materijala
TY  - JOUR
AU  - Ćosić, Milena
AU  - Aćimović-Pavlović, Zagorka
AU  - Terzić, Anja
AU  - Nedeljković, Borivoje
AU  - Pavlović, Ljubica
PY  - 2012
UR  - http://rims.institutims.rs/handle/123456789/179
AB  - Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests showed that two major changes of microstructural properties of rheocasting alloy, in comparison with conventional alloy, are change of dendrite morphology into nondendrite one and change of primary phases size (alpha-Al and Si). Both changes of primary particles were monitored in area near the stirrer and at a small distance from the crucible wall. Test showed that sizes of primary, alpha-Al particles decreased with stirring speed increment, while roundness of particles increased with stirring speed increment. Stirring speed change led to different degree of primary Si particles agglomeration. At stirring speed 1000 rpm, Si particles are uniformly distributed, while at speed 1500 rpm, a tendency to form clusters is more expressed. Test results were discussed on basis of utilizing fragmentation-agglomeration mechanism of primary phase evolution in a semi-solid melt, which may contribute to explanation of semi-solid structure development.
PB  - Editura Stiintifica Fmr, Bucharest
T2  - Metalurgia International
T1  - Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process
EP  - 93
IS  - 3
SP  - 88
VL  - 17
UR  - https://hdl.handle.net/21.15107/rcub_rims_179
ER  - 
@article{
author = "Ćosić, Milena and Aćimović-Pavlović, Zagorka and Terzić, Anja and Nedeljković, Borivoje and Pavlović, Ljubica",
year = "2012",
abstract = "Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests showed that two major changes of microstructural properties of rheocasting alloy, in comparison with conventional alloy, are change of dendrite morphology into nondendrite one and change of primary phases size (alpha-Al and Si). Both changes of primary particles were monitored in area near the stirrer and at a small distance from the crucible wall. Test showed that sizes of primary, alpha-Al particles decreased with stirring speed increment, while roundness of particles increased with stirring speed increment. Stirring speed change led to different degree of primary Si particles agglomeration. At stirring speed 1000 rpm, Si particles are uniformly distributed, while at speed 1500 rpm, a tendency to form clusters is more expressed. Test results were discussed on basis of utilizing fragmentation-agglomeration mechanism of primary phase evolution in a semi-solid melt, which may contribute to explanation of semi-solid structure development.",
publisher = "Editura Stiintifica Fmr, Bucharest",
journal = "Metalurgia International",
title = "Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process",
pages = "93-88",
number = "3",
volume = "17",
url = "https://hdl.handle.net/21.15107/rcub_rims_179"
}
Ćosić, M., Aćimović-Pavlović, Z., Terzić, A., Nedeljković, B.,& Pavlović, L.. (2012). Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process. in Metalurgia International
Editura Stiintifica Fmr, Bucharest., 17(3), 88-93.
https://hdl.handle.net/21.15107/rcub_rims_179
Ćosić M, Aćimović-Pavlović Z, Terzić A, Nedeljković B, Pavlović L. Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process. in Metalurgia International. 2012;17(3):88-93.
https://hdl.handle.net/21.15107/rcub_rims_179 .
Ćosić, Milena, Aćimović-Pavlović, Zagorka, Terzić, Anja, Nedeljković, Borivoje, Pavlović, Ljubica, "Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process" in Metalurgia International, 17, no. 3 (2012):88-93,
https://hdl.handle.net/21.15107/rcub_rims_179 .

DSpace software copyright © 2002-2015  DuraSpace
About RIMS | Send Feedback

OpenAIRERCUB
 

 

All of DSpaceCommunitiesAuthorsTitlesSubjectsThis institutionAuthorsTitlesSubjects

Statistics

View Usage Statistics

DSpace software copyright © 2002-2015  DuraSpace
About RIMS | Send Feedback

OpenAIRERCUB