Behaviour of nionikral-70 in low-cycle fatigue
(Institut za ispitivanje materijala, Beograd, 2017)
Experimental research on the behaviour of high-strength low-alloy steel ( HSLA)exposed to low-cycle fatigue (LCF) with controlled and fully reversible strain (Delta epsilon/2 = const, R epsilon =epsilon(min)/epsilon(max) ...
Experimental study on the stresses at the i-beam end-plate moment connection
(Institut za ispitivanje materijala, Beograd, 2019)
The paper deals with experimental study of the stresses at the bolted end-plate moment connection. The design parameters are adopted to include prying effects in joint. A stress level is obtained in the elements where the ...
Repair of cracks detected in cast components of vertical Kaplan turbine rotor hub
(Institut za ispitivanje materijala, Beograd, 2019)
During the revitalization of the hydroelectric generating station A4 at the hydro power plant 'Djerdap 1', all of its parts are subjected to non-destructive testing. Cracks are detected in cast part of generator rotor hub, ...
Structural integrity assessment of welded bucket-wheel boom
(Institut za ispitivanje materijala, Beograd, 2021)
Research is conducted on the causes of damage and the structural integrity assessment of the bucket-wheel boom welded lattice structures, before and after the repair of vital structures. Additionally, the paper describes ...
Integrity assessment of vital beam components that enable conjoint operation of two bridge cranes
(Institut za ispitivanje materijala, Beograd, 2018)
Vital components of the beam that enable conjoint operation of two bridge cranes are braces and threaded spindle. The beam connects two bridge cranes with overall lifting capacity of 500 t (2 × 250 t) and enables their ...
Analysis of causes of degradation of parent material and weld metal of breeches pipe at hydro power plant 'Perućica'
(Institut za ispitivanje materijala, Beograd, 2015)
Presented are results of non-destructive tests performed on the parent material and welded joints of structural parts of a breeches pipe (collar and anchor), and results of destructive tests performed on the parent material ...
Effect of locally damaged elbow segments on the integrity and reliability of the heating system
(Institut za ispitivanje materijala, Beograd, 2016)
This paper presents the integrity and reliability evaluation of the heating system as a whole, based on results of metallographic tests performed on parent material and the ultrasonic measurement of wall thickness of elbows ...
Probabilistic analysis of bearing capacity of piles with variable parameters in cpt test and calculation according to the requirements
(Institut za ispitivanje materijala, Beograd, 2016)
A probabilistic concept for determining pile bearing capacity is presented, taking into account the variability of CPT test parameters and methodology of calculation according to the requirements of Eurocode 7 (EN 1997-1: ...
Analiza loma spojnice lanca / Failure analysis of chain bracket
(Integritet i vek konstrukcija, Beograd, 2011)
Uprkos brojnim i skupim istraživanjima u oblasti zamora i loma kao i redovne kontrole gotovog proizvoda, prsline se javljaju svakodnevno u mnogim oblastima. Ovaj rad opisuje analizu otkaza spojnice lanca korišćene u konvejeru ...
Cracking resistance of AlMg4.5Mn alloy TIG welded joints
(Institut za ispitivanje materijala, Beograd, 2011)
In this paper the AlMg4.5Mn TIG welded joints have been tested in order to investigate their cracking resistance. Testing plates, size of 500×250×12 mm, are welded by TIG procedure in a horizontal-vertical position. Various ...