RIMS - Repository of Institute for Material Testing
Institute for Material Testing
    • English
    • Српски
    • Српски (Serbia)
  • English 
    • English
    • Serbian (Cyrillic)
    • Serbian (Latin)
  • Login
View Item 
  •   RIMS
  • Institut za ispitivanje materijala
  • Radovi istraživača / Researchers' publications
  • View Item
  •   RIMS
  • Institut za ispitivanje materijala
  • Radovi istraživača / Researchers' publications
  • View Item
JavaScript is disabled for your browser. Some features of this site may not work without it.

Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels

Thumbnail
Authors
Momčilović, Dejan
Atanasovska, Ivana
Milović, Ljubica
Odanović, Zoran
Conference object (Published version)
Metadata
Show full item record
Abstract
The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production. Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have some different fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue and stress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, and emphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will be discussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanning electron microscopy will be presented in this paper.
Keywords:
Corrosion / fatigue / stress corrosion cracking / low alloy steel
Source:
Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia, 2018, 129-
Publisher:
  • Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)
Related info:
  • Version of
    http://ecf22.rs

ISBN: 978-86-900686-0-9

[ Google Scholar ]
Handle
https://hdl.handle.net/21.15107/rcub_rims_473
URI
http://rims.institutims.rs/handle/123456789/473
Collections
  • Radovi istraživača / Researchers' publications
Institution/Community
Institut za ispitivanje materijala
TY  - CONF
AU  - Momčilović, Dejan
AU  - Atanasovska, Ivana
AU  - Milović, Ljubica
AU  - Odanović, Zoran
PY  - 2018
UR  - http://rims.institutims.rs/handle/123456789/473
AB  - The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.
Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have some
different fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue and
stress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, and
emphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will be
discussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanning
electron microscopy will be presented in this paper.
PB  - Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)
C3  - Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia
T1  - Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels
SP  - 129
UR  - https://hdl.handle.net/21.15107/rcub_rims_473
ER  - 
@conference{
author = "Momčilović, Dejan and Atanasovska, Ivana and Milović, Ljubica and Odanović, Zoran",
year = "2018",
abstract = "The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.
Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have some
different fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue and
stress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, and
emphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will be
discussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanning
electron microscopy will be presented in this paper.",
publisher = "Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)",
journal = "Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia",
title = "Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels",
pages = "129",
url = "https://hdl.handle.net/21.15107/rcub_rims_473"
}
Momčilović, D., Atanasovska, I., Milović, L.,& Odanović, Z.. (2018). Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels. in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia
Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)., 129.
https://hdl.handle.net/21.15107/rcub_rims_473
Momčilović D, Atanasovska I, Milović L, Odanović Z. Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels. in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia. 2018;:129.
https://hdl.handle.net/21.15107/rcub_rims_473 .
Momčilović, Dejan, Atanasovska, Ivana, Milović, Ljubica, Odanović, Zoran, "Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels" in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia (2018):129,
https://hdl.handle.net/21.15107/rcub_rims_473 .

DSpace software copyright © 2002-2015  DuraSpace
About RIMS | Send Feedback

OpenAIRERCUB
 

 

All of DSpaceCommunitiesAuthorsTitlesSubjectsThis institutionAuthorsTitlesSubjects

Statistics

View Usage Statistics

DSpace software copyright © 2002-2015  DuraSpace
About RIMS | Send Feedback

OpenAIRERCUB