Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process
(Editura Stiintifica Fmr, Bucharest, 2012)
Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests ...
The possibility of substitution of wear resistant low chromium white iron resistant with basalt melt
(Editura Stiintifica Fmr, Bucharest, 2012)
In this study the testing results of the possibility of substituting mill lining plates for ore milling made of low chromium white iron that is resistant to wear with plates made of basalt melt are presented. Plates made ...