Experimental Determination of JIc for a HSLA Steel Welded Joint
(Elsevier B.V., 2023)
Most serious weldment failures have catastrophic consequences in terms of damage to other equipment, loss of production, and risks to worker health and safety. For the above reasons, there is a tendency to find the line ...
Experimental Determination of JIc for a HSLA Steel Welded Joint
(2nd International Symposium on Risk Analysis and Safety of Complex Structures and Components (IRAS 2023), 2023)
Most serious weldment failures have catastrophic consequences in terms of damage to other equipment,
loss of production, and risks to worker health and safety. For the above reasons, there is a tendency to find the
line ...
Determination of polynomial depending between hardness and cooling time t8/5 of steel NIONICRAL 70 heat affected zone
(18th International Conference on New Trends in Fatigue and Fracture NT2F18, 2018)
Because of the high heating and cooling velocity values, welding procedure is an unstable process. During
welding, changes in microstructure are occurring under overheating and/or cooling conditions. In comparing to ...
Methodology for determining the region of stabilization of low-cycle fatigue
(Fakultet strojarstva i brodarsta, Univerzitet u Zagrebu, Hrvatska, 2016)
In present paper, the behaviour of high-strength low-alloyed (HSLA) steel under conditions
of low-cycle fatigue (LCF) has been experimentally tested and analyzed. Based on the experimental
results obtained in the programme ...
Processing of Data Obtained by the Testing of Steel under Low Cyclic Fatigue (Part I)
(University of Zagreb Faculty of Mechanical Engineering and Naval Architecture, 2022)
The design of mechanical components exposed to fatigue load, at a low number of cycles, requires knowledge of the behaviour of the material under the impact of variable load in conditions of controlled strain when cyclic ...
Determining of the Fatigue Crack Growth Rate of HSLA Steel at Room Temperature
(Advanced Technologies & Materials, 2022)
Welded joint is a critical region of a welded structure and fracture mechanics analysis is inevitable
in the structural integrity assessment of all welded structures. This paper shows the determining of
parameters of the ...
Experimental Determination of the Critical Value of the J-Integral that Refers to the HSLA Steel Welded Joint
(Strojarski Facultet, 2023)
Fracture mechanics, as a scientific discipline dealing with the study of cracks in welded structures, has defined parameters and introduced new test methods in order to better determine the tendency to crack growth, critical ...
Assessment of the behaviour of fatigue loaded HSLA welded steel joint by applying fracture mechanics parameters
(New Trends in Fatigue and Fracture NT2F12, Brasov, Romania, Proceedings, 2012)
In discussion of the welded joints from fracture mechanics point of
view, it is assumed that the welded joint is pre-cracked and that therefore fatigue life
of the pre-cracked structure is determined by the period of ...
Procena ponašanja zavarenog spoja HSLA čelika opterećenog na zamor primenom parametara mehanike loma / Assessment of the behaviour of fatigue loaded HSLA steel welded joint by applying fracture mechanics parameters
(Institut za ispitivanje materijala, Beograd, 2012)
U zavarenim spojevima, sa gledišta mehanike loma, se pretpostavlja prisustvo prslina, gde se onda vek s obzirom na zamor takvih konstrukcija sa prslinama procenjuje vremenom rasta prsline pod promenljivim opterećenjem. ...
Identification of low cycle fatigue parameters of high strength low-alloy (HSLA) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...