Investigation of the Repair Welding Technology Using Ni Base Electrode
(Trans Tech Publications Ltd, Durnten-Zurich, 2013)
Metal materials are subjected to innumerable time-dependent degradation mechanisms when operate in power, petrochemical and refinery plant. These materials are subjected to multiaxial stresses, creep, fatigue, corrosion ...
The influence of corrosion on stress concentration factor at shaft to flange radius
(Springer Netherlands, 2013)
This paper describes the influence of corrosion on stress concentration factor and crack initiation at shaft-flange transition section. The real turbine shaft failure case study is used for research. This case study and ...
State Analysis and Integrity of Welded Structures of the Upper Ring of the Turbine Runner Guide Vane Apparatus of Hydroelectric Generating Set A6 on Hydro Power Plant Djerdap 1
(Trans Tech Publications Ltd, Durnten-Zurich, 2013)
During the refurbishment of the hydroelectric generating set A6 on HPP "Djerdap 1", for the state analysis and assessment of the level and causes of degradation of the structure of the vertical Kaplan turbine runner guide ...
Drying Process Modelling for Heavy Clay Products Using a New Thin Layer Drying Model
(Trans Tech Publications Ltd, Stafa-Zurich, 2013)
Drying results, determined on samples made of masonry clay from the locality "Banatski Karlovac", are presented in this study. Experimental investigations were carried out in a laboratory recirculation dryer in which drying ...
Control of hazardous waste in the laboratory for metal testing-current problems / Kontrolisanje opasnog otpada u laboratoriji za ispitivanje metala - aktuelni problemi
(Udruženje inženjera Srbije za koroziju i zaštitu materijala, Srbija, 2013)
This paper presents a controlled process of collecting, identification, classification and labeling of waste and
hazardous materials in laboratory for testing materials of the Institute of testing materials {Institute ...
Testing of metals in the function of determining the failure of turbine shaft – methodological approach
(Unversity of Banja Luka, Faculty of Mechanical Engineering, BiH, 2013)
This paper presents a methodological approach of testing of metals in the
function of determining the cause of failure and failure analysis of turbine shaft. The
analysis was conducted on the example of damage of the ...
NDT in function prevention of loss integrity of structures large dimensions
(Association of Mining and Geological Engineers of Macedonia, 2013)
Developing a methodology for the integrated numerical evaluation and performance assessment of soil-pile-pier
(Higher School of Civil Engineering (VSU) 'Lyuben Karavelov' - Sofia, Bugarska, 2013)
In the paper is developed a discrete numerical solid pile model with a discontinuity and defects. Model included performance-based seismic evaluation of the soil-pile-bridge pier interaction. The pile discontinuity and ...
Methodological approach to recovery of damages of the steamlines in thermal power plants and heating plants / Metodološki pristup sanaciji oštećenja parovoda u termoelektranama i toplanama
(Tehnološki fakultet Zvornik, BiH, 2013)
Na primeru procurivanja i ostecenja parovoda sveze pare u termoelektranama i toplanama
prikazan je metodoloski pristup utvrdivanja uzroka otkaza i saniranja ostecenja. Dati pristup se
moze primeniti za slicne konstrukcije, ...
NDT in function prevention of loss integrity of structures large dimensions
(Association of Mining and Geological Engineers of Macedonia, 2013)