J-integral Analysis of the Simulated Heat-affected Zone of the Elevated-temperature Martensitic Steel
(Springer, New York, 2021)
Due to its superior strength at high temperatures P/T91 steel is often applied in the chemical, petrochemical and fossil-fired power generation industries. The high strength is achieved by a suitable martensitic microstructure ...
Numerical simulation of fatigue crack propagation: A case study of defected steam pipeline
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
In order to prevent the premature failure of steam pipeline produced of molybdenum-vanadium steel, the experimental tests were performed to measure fracture toughness and to determine the mechanical behaviour of cracked ...
Numerical determination and experimental validation of the fracture toughness of welded joints
(Pergamon-Elsevier Science Ltd, Oxford, 2020)
Most of the serious weldment failures lead to catastrophic consequences in terms of damage of other equipment, loss of production, and risks to workers' health and safety. Hence, there is motivation to find margin between ...
Experimental and numerical investigations of the critical values of J-integral for the steel of steam pipelines
(Elsevier Science Bv, Amsterdam, 2018)
Steel grade 14MoV6-3 is a low-carbon microalloyed steel with addition of chromium and molybdenum. This grade is designed mainly for power industry applications, withstanding operating at elevated temperatures.In this paper, ...
Experimental determination and numerical validation of the critical value of the J-integral ofa low carbon microalloyed steel for elevated temperature application
(VIII INTERNATIONAL CONGRESS ENGINEERING, ENVIRONMENT AND MATERIALS IN PROCESS INDUSTRY EEM 2023, 2023)
To evaluate the behavior of a homogeneous material in the presence of a crack-type defect, the
value of the critical stress-intensity factor, KIc, was determined as a measure of the fracture
toughness of the tested steel ...
Experimental Determination of the Critical Value of the J-Integral that Refers to the HSLA Steel Welded Joint
(Strojarski Facultet, 2023)
Fracture mechanics, as a scientific discipline dealing with the study of cracks in welded structures, has defined parameters and introduced new test methods in order to better determine the tendency to crack growth, critical ...
Experimental Determination of JIc for a HSLA Steel Welded Joint
(Elsevier B.V., 2023)
Most serious weldment failures have catastrophic consequences in terms of damage to other equipment, loss of production, and risks to worker health and safety. For the above reasons, there is a tendency to find the line ...
Experimental Determination of JIc for a HSLA Steel Welded Joint
(2nd International Symposium on Risk Analysis and Safety of Complex Structures and Components (IRAS 2023), 2023)
Most serious weldment failures have catastrophic consequences in terms of damage to other equipment,
loss of production, and risks to worker health and safety. For the above reasons, there is a tendency to find the
line ...
Assessment of the behaviour of fatigue loaded HSLA welded steel joint by applying fracture mechanics parameters
(New Trends in Fatigue and Fracture NT2F12, Brasov, Romania, Proceedings, 2012)
In discussion of the welded joints from fracture mechanics point of
view, it is assumed that the welded joint is pre-cracked and that therefore fatigue life
of the pre-cracked structure is determined by the period of ...