Process parameters influence on microstructural properties of hypereutectic al-18wt% Si alloys obtained by rheocasting process
(Editura Stiintifica Fmr, Bucharest, 2012)
Hypereutectic Al-18wt%Si alloy was obtained by conventional and rheocasting procedure at cooling rate 0.16 +/- 0.05 degrees Cs-1. Samples of rheocasted alloy were obtained at two stirring speeds 1000 and 1500 rpm. Tests ...
Veza između mikrostrukture, faznog sastava i mehaničkih svojstava termo-izolacionih veziva na bazi otpadnog materijala / Correlation between microstructure, phase composition and mechanical properties of thermo-insulation bonding agents based on waste material
(Univerzitet u Nišu, Niš, 2012)
Konstrukcioni kompoziti - termo-izolaciona i/ili visoko-temperaturna veziva u kojima je leteći pepeo, kao potencijalno štetna materija za okolinu, kombinovan sa običnim i vatrostalnim cementom predstavlja jednu sasvim novu ...
The possibility of substitution of wear resistant low chromium white iron resistant with basalt melt
(Editura Stiintifica Fmr, Bucharest, 2012)
In this study the testing results of the possibility of substituting mill lining plates for ore milling made of low chromium white iron that is resistant to wear with plates made of basalt melt are presented. Plates made ...