Procena ponašanja zavarenog spoja HSLA čelika opterećenog na zamor primenom parametara mehanike loma / Assessment of the behaviour of fatigue loaded HSLA steel welded joint by applying fracture mechanics parameters
(Institut za ispitivanje materijala, Beograd, 2012)
U zavarenim spojevima, sa gledišta mehanike loma, se pretpostavlja prisustvo prslina, gde se onda vek s obzirom na zamor takvih konstrukcija sa prslinama procenjuje vremenom rasta prsline pod promenljivim opterećenjem. ...
Identification of low cycle fatigue parameters of high strength low-alloy (HSLA) steel at room temperature
(Croatian Metallurgical Soc, Zagreb, 2014)
Low cycle fatigue test was performed in ambient atmosphere at room temperature. cycle loading of material, in case of High strength low-alloy steel, entails modifications of its properties and in this paper is therefore ...
Cavitation damages morphology of high-strength low-alloy steel
(Faculty of Metallurgy, 2016)
This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in ...
Impact of choice of stabilized hysteresis loop on the end result of investigation of high-strength low-alloy (HSLA) steel on low cycle fatigue
(Croatian Metallurgical Soc, Zagreb, 2014)
High strength low-alloy steel under low cycle fatigue at a certain level of strain controlled achieve stabilized condition. During the fatigue loading stabilized hysteresis loop is determined, which typical cycle of ...
Experimental Determination of JIc for a HSLA Steel Welded Joint
(Elsevier B.V., 2023)
Most serious weldment failures have catastrophic consequences in terms of damage to other equipment, loss of production, and risks to worker health and safety. For the above reasons, there is a tendency to find the line ...
Processing of Data Obtained by the Testing of Steel under Low Cyclic Fatigue (Part I)
(University of Zagreb Faculty of Mechanical Engineering and Naval Architecture, 2022)
The design of mechanical components exposed to fatigue load, at a low number of cycles, requires knowledge of the behaviour of the material under the impact of variable load in conditions of controlled strain when cyclic ...
Experimental Determination of the Critical Value of the J-Integral that Refers to the HSLA Steel Welded Joint
(Strojarski Facultet, 2023)
Fracture mechanics, as a scientific discipline dealing with the study of cracks in welded structures, has defined parameters and introduced new test methods in order to better determine the tendency to crack growth, critical ...
Determining of the Fatigue Crack Growth Rate of HSLA Steel at Room Temperature
(Advanced Technologies & Materials, 2022)
Welded joint is a critical region of a welded structure and fracture mechanics analysis is inevitable
in the structural integrity assessment of all welded structures. This paper shows the determining of
parameters of the ...