Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production.
Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have some
different fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue and
stress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, and
emphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will be
discussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanning
electron microscopy will be presented in this paper.
Кључне речи:
Corrosion / fatigue / stress corrosion cracking / low alloy steelИзвор:
Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia, 2018, 129-Издавач:
- Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)
Повезане информације:
- Верзија документа
http://ecf22.rs
Институција/група
Institut za ispitivanje materijalaTY - CONF AU - Momčilović, Dejan AU - Atanasovska, Ivana AU - Milović, Ljubica AU - Odanović, Zoran PY - 2018 UR - http://rims.institutims.rs/handle/123456789/473 AB - The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production. Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have some different fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue and stress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, and emphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will be discussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanning electron microscopy will be presented in this paper. PB - Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK) C3 - Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia T1 - Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels SP - 129 UR - https://hdl.handle.net/21.15107/rcub_rims_473 ER -
@conference{ author = "Momčilović, Dejan and Atanasovska, Ivana and Milović, Ljubica and Odanović, Zoran", year = "2018", abstract = "The fracture surface appearances are slowly changed through decade’s side by advantages in technology of steel production. Basic requirements for cleaner steels and lower energy consumption during production induce that newer steels have some different fracture features compared to the old ones. This paper describes morphology of different corrosion fatigue and stress corrosion cracks. The brief failure analysis with key results will be presented for each case mentioned in paper, and emphasize will be on morphology and characteristic features of fracture surfaces. Macro appearance of fatigue cracks will be discussed in detail and characteristic features of stress corrosion fractures will be analyzed. Also, the results from scanning electron microscopy will be presented in this paper.", publisher = "Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)", journal = "Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia", title = "Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels", pages = "129", url = "https://hdl.handle.net/21.15107/rcub_rims_473" }
Momčilović, D., Atanasovska, I., Milović, L.,& Odanović, Z.. (2018). Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels. in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia Society for Structural Integrity and Life – Prof. Dr Stojan Sedmak (DIVK)., 129. https://hdl.handle.net/21.15107/rcub_rims_473
Momčilović D, Atanasovska I, Milović L, Odanović Z. Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels. in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia. 2018;:129. https://hdl.handle.net/21.15107/rcub_rims_473 .
Momčilović, Dejan, Atanasovska, Ivana, Milović, Ljubica, Odanović, Zoran, "Morphology of corrosion fatigue and stress corrosion cracks on low alloy steels" in Book of abstracts - 22nd European Conference on Fracture - ECF22: LOADING AND ENVIRONMENT EFFECTS ON STRUCTURAL INTEGRITY, Belgrade, Serbia (2018):129, https://hdl.handle.net/21.15107/rcub_rims_473 .