Now showing items 11-20 of 21
Residual life estimation of a thermal power plant component: The high-pressure turbine housing case
(Univerzitet u Beogradu - Institut za nuklearne nauke Vinča, Beograd, 2009)
This study focuses on the estimation of residual life of damaged thermal power plant components. The high-pressure turbine housing was chosen as an example of thermal power plant component where, during the years of ...
Influence of increased temperature on clay fast drying process
(Revista Romana de Materiale/ Romanian Journal of Materials, 2009)
In this paper are presented testing results during process of fast drying at conditions of increased temperature. Three different masonry raw materials were examined using recircular laboratory dryer with air recirculation. ...
Veza između mehaničkih svojstava i mikrostrukture vatrostalnih kompozita određena nedestruktivnim metodama ispitivanja / Correlation between mechanical properties and microstructure of refractory composites determined using non-destructive testing method
(Društvo za ispitivanje i istraživanje materijala i konstrukcija Srbije, Beograd, 2009)
Cilj ovog rada je da se utvrdi veza između važnih mehaničkih svojstava i karakteristika mikrostrukture pomoću nedestruktivne ispitne metode - metode merenja berzine ultrazvuka, na uzorcima korundnih i boksitnih vatrostalnih ...
Analitička procena mogućnosti primene interventnog reparaturnog zavarivanja čelika 13CrMo 4-5 / Analytical estimation of the application potentials for the emergency repair welding of the 13CrMo 4-5 steel
(DUZS - Društvo za unapređivanje zavarivanja u Srbiji, Beograd, 2009)
Čelik 13CrMo 4-5 (~Č7400) već dugi niz godina se primenjuje za izradu delova termoenergetskih postrojenja kao što su elementi kotlova i cevi. On spada u grupu niskolegiranih konstrukcionih čelika za rad na povišenim ...
Correlation among sintering process, porosity, and creep deformation of refractory concrete
(Springer, New York, 2009)
The aim of this paper is to establish the correlation among sintering process, porosity, and important thermo-mechanical property of refractory concrete, i.e., creep. Creep deformation was investigated according to the ...
Methodical approach to identification and quantification of corrosion damages of corrosion the casing steel tubes in petroleum industry
(University of East Sarajevo, Faculty of Technology, 2009)
Methodological approach of identification and quantification of corrosion damages of the steel tubes which use for casing the well in petroleum industry are presented in the paper. A description and consequence of steel ...
Karakterizacija muljeva od neutralizacije otpadnih rastvora i ispirnih voda iz postupka toplog cinkovanja / Characterization of sludge from neutralization of waste solutions and rinsing waters in hot dip galvanizing processes
(Inženjersko društvo za koroziju, Beograd, 2009)
Muljevi nastali rešavanjem otpadnih voda i istrošenih rastvora od pripreme u pogonu toplog cinkovanja spadaju u grupu opasnog industrijskog otpada. Upravljanje ovom vrstom otpada složen je i delikatan posao. Prvi važan ...
Hronologija gubitka integriteta konstrukcija zbog grešaka izrade zavarenih konstrukcija / Chronology of lost structural integrity initiated from manufacturing defects in welded structures
(Institut za ispitivanje materijala, Beograd, 2009)
U različitim vremenskim periodima dolazilo je do gubitka integriteta zavarenih konstrukcija zbog razvoja proizvodnih grešaka zavarenog spoja. Mehanizmi otkaza su bili različiti i uvek su predstavljali novo iskustvo, koje ...
Failure analysis of the end eye connection of the bucket wheel excavator portal tie-rod support
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
This paper describes the failure analysis results of the bucket wheel excavator (BWE) portal tie-rod support. The results of finite elements analysis (FEA) point out the occurrence of pronounced stress concentration, whereby ...
Mogućnost primene recikliranog agregata u projektovanju betona i metode ispitivanja svojstva betona
(Tehnika Naše građevinarstvo, 2009)