Study on impact properties of creep-resistant steel thermally simulated heat affected zone
(Univerzitet u Beogradu - Institut za nuklearne nauke Vinča, Beograd, 2012)
The steam pipe line and steam line material, along with its welded joints, subject to damage that accumulates during operation in coal power plants. As a result of thermal fatigue, dilatation of steam pipe line at an ...
Methodology for reparation of damaged sleeves and welded shield sections of guide vanes at hydropower plant DJERDAP 1
(Trans Tech Publications Ltd, 2014)
Vertical Kaplan turbines, manufactured in Russia and with nominal power of 200 MW, have been installed in 6 hydroelectric generating units at ’Djerdap 1’. During the refurbishment of hydropower plant experimental non-destructive ...
Prediction and Optimization of Heavy Clay Products Quality
(Wiley Blackwell, 2014)
The effects of chemical composition, firing temperature (800-1100 °C), and several shape formats of laboratory brick samples on the final product quality were investigated. Prediction of the final laboratory products ...
Sensitivity analysis of mathematical models for final product properties: Link to DTG curve
(Elsevier Sci Ltd, Oxford, 2013)
Compressive strength and water absorption of fired heavy clay products varies with firing temperatures, but not entirely according to linear function, as it is mostly reported in literature. Also, differential thermo-gravimetric ...
Failure investigation of the bucket wheel excavator crawler chain link
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The high mobility of open pit machines in heavy duty conditions provides fertile ground for the occurrence of various failures of the traveling mechanisms' vital parts such as chain links. The goal of the study presented ...
Determination of critical size of corrosion pit on mechanical elements in hydro power plants
(Udruženje intelektualaca za razvoj nauke u Srbiji, Novi Sad, 2018)
Researchers in the field of fracture mechanics, predominantly developing appropriate solution algorithms for problems of solid bodies with cracks. Problems in mechanics generally, related with fracture and fatigue for solid ...
Quantification of stress raiser influence on decrease of machine parts fatigue life
(Univ Novi Sad, Fac Tech Sci, Adeko, Novi Sad, 2012)
This paper displays the usage of Theory of Critical Distances (TCD) in the prediction of high-cycle fatigue behaviour in machine parts and systems. It is possible to gain real overview of stresses of machine parts by Finite ...
Explicit parametric method for optimal spur gear tooth profile definition
(Trans Tech Publications Ltd, 2013)
The gear tooth profile has an immense effect on the main operating parameters of gear pairs (load capacity, working life, efficiency, vibrations, etc). In current engineering research and practice, there is a strong need ...
The influence of corrosion on stress concentration factor at shaft to flange radius
(Springer Netherlands, 2013)
This paper describes the influence of corrosion on stress concentration factor and crack initiation at shaft-flange transition section. The real turbine shaft failure case study is used for research. This case study and ...
Prediction of crack initiation in spur gear contact zone
(Univ Novi Sad, Fac Tech Sci, Adeko, Novi Sad, 2012)
The objective of this paper is to give a new viewpoint in contact fatigue prediction in the case of high-cycle fatigue. The presented research is based on up-to-date methods and multidisciplinary approach, and enables ...